52100 100Cr6 SUJ2 Bearing Steel Bar

52100 100Cr6 SUJ2 Bearing Steel Bar

Categories:Steel Bars

Model No.:100Cr6

Size: 10-350mm

Length: as your request.

Delivery condition: hot rolled/normalized/quenched&tempered.

Surface: black/peeled/turned/grinding..

DETAIL INFORMATION

52100 100Cr6 SUJ2 Bearing Steel Bar


52100 steel is a deep hardening alloy used for aircraft bearings or other high stressed parts where good rolling contact fatigue strength is required at temps below 400 degrees. The 52100 vac melt steel material offers superior cleanliness and internal soundness over the conventional air melted SAE 52100.

 

52100 is a through hardening bearing steels intended for rolling contact and other high fatigue applications. In the hardened condition the high hardness, high strength and high cleanliness provides the steel with the right properties to withstand high cycle, high stress fatigue. 52100 is mainly used for small and medium sized bearing components. It is also regularly used for other machine components that require high tensile strength and high hardness.

 

52100 Round Bars bearing steel is one kind of special steel with features of high wear resistance and rolling fatigue strength. High-carbon chromium bearing steel, engineering steel and some types of stainless steel and heat resistant steel are used as materials of bearings and for other purposes.

 

Advantages of Chrome Bearing Steel 52100:

Superior hardness, 60-67 on Rockwell hardness scale (Rc) at room temperature

High carbon chrome alloy steel

Operates continually at temperatures up to 120°C

Used to produce precision ball bearings and roller bearings

Cost-effective

Long working life

 

Applications of 52100 Bearing Steel

Alloy steel 52100 grade bearing steel is mainly used for the manufacture of aircraft bearings and other highly stressed parts. This steel grade 52100 steel is preferably vacuum arc re-melted to give optimum performance. Typical applications: Bearing Manufacture, CV joints, ball screws, gauges, knife etc.

 

Comparable Standards:

AISI/SAEDINJISGB
52100100Cr6SUJ2GCr15


52100 Chemical Composition

CSiMnPSCrNiCu
0.95-1.050.15-0.350.25-0.45≤0.025≤0.0251.4-1.6≤0.25≤0.25


Mechanical Properties of ASTM A295 52100 Bearing Steel

Properties

Metric

Imperial

Bulk modulus (typical for steel)

140 GPa

20300 ksi

Shear modulus (typical for steel)

80 GPa

11600 ksi

Elastic modulus

190-210 GPa

27557-30458 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Hardness, Brinell

Hardness, Knoop (converted from Rockwell C hardness)

875

875

Hardness, Rockwell C (quenched in oil from 150°C tempered)

62

62

Hardness, Rockwell C (quenched in water from 150°C tempered)

64

64

Hardness, Rockwell C (quenched in oil)

64

64

Hardness, Rockwell C (quenched in water)

66

66

Hardness, Vickers (converted from Rockwell C hardness)

848

848

Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel)

40

40

 

52100 Heat Treatment

AISI 52100 alloy bearing steel is heated at 816°C followed by quenching in oil. Before performing this process, it is subjected to normalizing heat treatment at 872°C followed by slowly cooling in order to reduce the machining stress.

AISI 52100 bearing steels alloy can be hot worked at 205 to 538°C.

AISI 52100 bearing steel can be cold worked using conventional techniques in the annealed or normalized conditions.

AISI 52100 alloy bearing steel could be hardened by quenching in water from 801-829 degree or quench in oil from 816-842 degree.

Temper to desired hardness as indicated by tempering curves after water or oil quench.


Products Related

Enquiry

Company*

Name*

Phone

Email*

Want to know more?

If you want to know more or have any questions about our products, please feel free to contact us by phone or email.