Categories：Steel Bars
Model No.:1.2601 X165CrMoV12
Size: 10-350mm
Delivery condition: hot rolled/ hot forged.
Surface: black/rough turned.
1.2601 X165CrMoV12 Cold Work Tool Steel
X165CrMoV12 1.2601 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number 1.2601. Metal Steel Grade W-Nr X165CrMoV12 It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold.
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working
rolls , measuring tools .
Germany | Italy | Sweden | Spain |
DIN,WNr | UNI | SS | UNE |
X165CrMoV12 | 1.2601 | X165CRMOW12KU | 2310 | X160CRMOV12 |
C | Si | Mn | P | S | Cr | Mo | Other |
1.55-1.75 | 0.25-0.40 | 0.20-0.40 | 0.030 | 0.030 | 11.0-12.0 | 0.50-0.70 | V 0.10-0.50 |
Rp0.2 (MPa) | Rm (MPa) | Impact | Elongation | A Z (%) | Delivery | Hardness HB |
641 (≥) | 662 (≥) | 23 | 14 | 31 | Solution & Aging, Ann, Ausaging, Q+T | 142 |
Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
Quenching: Hardening temperature/℃: 980~1010, Quenching in oil or air
Tempering: Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
Normalizing：at Normalizing temperature, then cool in furnace
AISI 1035,Cold Drawn Carbon Hexagonal Bar
4145H Modified Alloy Steel Round Bar, Hot Rolled Steel Bar
SAE 4137H Alloy Steel Bar
AISI 4130 75K P+X Alloy Steel Bar
QT AISI 8260 Hot Rolled Steel Round Bar Size 10 - 350mm For Automobile
ASTM 1045 Hot Rolled Steel Bar , Carbon Steel Round Bar / Rod 10 - 350mm
If you want to know more or have any questions about our products, please feel free to contact us by phone or email.